An observation of accelerated exfoliation in iPP/organoclay nanocomposite as induced by repeated shear during melt solidification

A well‐exfoliated morphology is usually observed for polar polymer/clay nanocomposites via dynamic melt processing techniques, whereas only an intercalated or a partially intercalated/partially exfoliated morphology is often obtained for nonpolar polymer/clay nanocomposites, even though some polar compatibilzer is used. In this study, an accelerated exfoliation effect was observed for the first time in iPP/organoclay nanocomposites prepared through so‐called dynamic packing injection molding, in which the specimen is forced to move repeatedly in a chamber by two pistons that move reversibly with the same frequency as the solidification progressively occurs from the mold wall to the molding core part. The disordered level and exfoliated degree of clay was found to dramatically increase from the skin to the core of the prepared samples and eventually the WAXD reflections of interlayer d‐spacing diminished in the core. The changed degree of exfoliation was also proved directly by TEM observation. The prolongation of processing time, the gradual growth of solidification front, the increased melts viscosity, and the shear amplification effect were considered to explain the higher degree of exfoliation in the center zone of mold chamber. Our result suggests that a critical shear force may be needed to break down clay into exfoliated structure. This can be also well used to explain at least partially the intercalated morphology, which is commonly observed for nonpolar polymer/clay nanocomposites via conventional processing. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 2005–2012, 2005