Ba8ZnTa6O24: A New High Q Dielectric Perovskite

The hexagonal perovskite, Ba8ZnTa6O24, was prepared in single‐phase form and was found to be a stable secondary phase, formed as a result of the loss of ZnO from Ba(Zn1/3Ta2/3)O3 microwave dielectrics. The experimental and calculated X‐ray patterns of Ba8ZnTa6O24 indicate it is isostructural with Ba8Ta6NiO24 with an 8H (cchc)2 close‐packed BaO3 stacking sequence and the lattice parameters, a=10.0825(14), c=19.0587(38)Å. High‐density ceramics of Ba8ZnTa6O24 could be prepared at temperatures considerably lower (1400°C) than those used to sinter pure Ba(Zn1/3Ta2/3)O3, and exhibit very good microwave dielectric properties with ɛ=30.5, Qf=62 300, and τf=+36 ppm/°C at 8.9 GHz.