Effect of Heat Treatment on Mechanical Properties of Nickel-Titanium Instruments

The aim of this study was to evaluate the torsional resistance, cyclic fatigue resistance, and bending stiffness of nickel-titanium (NiTi) file systems with different heat treatments and cross-sectional designs. WaveOne Primary treated with memory-triple (MT) heat treatment (WOMT) was compared with WaveOne Primary (WO) and WaveOne Gold Primary (WOG). Torsional resistance test was performed using a customized device, and the distortion angle, ultimate strength, and toughness were evaluated. For cyclic fatigue resistance test, the instruments were reciprocated with continuous 4 mm up-and-down movement until fracture in a customized device, and the time to fracture was compared. Fracture surfaces of each group were examined under the scanning electron microscope. Bending stiffness was measured using a custom-made device. The results were analyzed using one-way analysis of variance and the Tukey's post hoc comparison at a significance level of 95%. WOMT showed higher ultimate strength and toughness than the other systems (P