Strength and flexibility of bulk high-T)c) superconductors

Strength, fracture toughness, and elastic modulus data for bulk high-temperature superconductors, commercial 99.9% Ag, and a 1.2 at.% Mg/Ag alloy have been collected. These data have been used to calculate fracture strains for bulk conductors. The calculations indicate that the superconducting cores of clad tapes should begin to fracture at strains below 0.2%. In addition, residual strains in Ag-clad (Bi,Pb))2)Sr)2)Ca)2)Cu)3)O)x ) tapes have been measured by neutron diffraction. An explanation is offered for why many tapes appear to be able to tolerate large strains before exhibiting a reduction in current transport