Research of long IBADPLD coated conductors with high quality

Continuous processes using Ion-Beam-Assisted Deposition (IBAD) and Pulsed-Laser-Deposition (PLD). Biaxially textured Gd2Zr2O7 buffer layers up to 255 m long were fabricated by IBAD with the production speed of 0.5-1.0 m/h. Y-123 films were formed on them by PLD with the tape speed of 1.0-4.0 m/h. A 105 m long Y-123 film was formed with the uniform thickness of 1.0 mum and the AO of 3-4DG. The end-to-end Ic of 126 A was achieved at 77 K, 0 T, whose / V curve had the n-value of 28.5. The times length reached 13,230 Another 70 m long Y-123 tape with the Ic of over 90 A (77 K, 0 T) was wound into a solenoid type magnet whose inner diameter was 60 mm. The central magnetic field of 0.082 T was obtained at 77 K, with operating current of 42 A and that of 0.27 T was obtained at 66 K, with operating current of 130 A.