The influence of surface treatments in hot acid solutions on the corrosion resistance and oxide structure of stainless steels

The influence of surface treatments in hot acid solutions on the corrosion resistance and oxide structure of stainless steels

The effect of anodic treatments on the corrosion resistance in Cl −-solutions and the structure of oxide layers on alloy AISI304 was investigated. Oxides were analysed using RBS, SEM and TEM. The highest pitting potential shifts (790 mV) are obtained by anodizing at high temperature (95 °C) within t...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Corrosion science 2005-03, Vol.47 (3), p.757-769
Hauptverfasser: Taveira, L.V., Frank, G., Strunk, H.P., Dick, L.F.P.
Format: Artikel
Sprache:eng
Schlagworte:
Anodization
Applied sciences
Corrosion
Corrosion environments
Corrosion mechanisms
Exact sciences and technology
Metals. Metallurgy
Pitting corrosion
Stainless steels
Surface treatments
TEM
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The effect of anodic treatments on the corrosion resistance in Cl −-solutions and the structure of oxide layers on alloy AISI304 was investigated. Oxides were analysed using RBS, SEM and TEM. The highest pitting potential shifts (790 mV) are obtained by anodizing at high temperature (95 °C) within the passive range in acid baths. Using this method it was possible to grow oxides layers up to 400 nm, that are constituted of porous nanocrystalline spinel. Mo and Nb are incorporated into the oxide layer but have no benefit on the improvement of corrosion resistance, which is explained by greater thickness and Cr-enrichment of the oxide layer.