Effect of sintering time on microstructure and optical properties of yttria-partially stabilized monolithic zirconia

To evaluate the impact of speed sintering on the microstructure and optical properties of 3 and 5 mol% yttria-partially stabilized monolithic zirconias. 120 plate-shaped zirconia specimens (10x10x 0.4 mm) were prepared from three commercial 5 mol% yttria-partially stabilized zirconia blocks (5Y-PSZs); Katana UTML (Kuraray Noritake), Cercon xtML (Dentsply Sirona), and Zolid FX white (Amann Girrbach), and two commercial 3 mol% yttria-partially stabilized zirconia blocks (3Y-PSZs); Lava Plus (3 M ESPE) and InCoris (Sirona, GmbH). Specimens were either conventional sintered (CS) using a 7-hour program or speed sintered (SS) using a quick 90-minute program. The microstructure was inspected with a scanning electron microscope (SEM), and phase fractions were detected using x-ray diffraction analysis (XRD). Translucency (TP00), and contrast ratio (CR) were obtained using a spectrophotometer (VITA Easyshade V). Color difference (ΔE00) between both sintering processes was calculated with the CIEDE2000 formula. ΔE00 up to 1.8 was set as the acceptability threshold. Data were analyzed using two-way ANOVA, Krusakll-Wallis, and Mann-Whitney U tests. (n = 12, α = .05). Grain size was significantly decreased after SS for all tested materials (P