Preparation of agar functionalized graphene oxide-immobilized copper ferrite aerogel for dye degradation via dark-Fenton oxidative process

Dye and textile industries are one of the main causes of water pollution and put the environment and health of society at risk. Developing new materials to decontaminate industrial waste effluents containing dyes as pollutants is challenging due to numerous issues, including tailoring recyclable and biodegradable agents. This study focuses on applying an advanced oxidation process, electro-Fenton for the treatment of dye-containing wastewater using agar-functionalized graphene oxide-immobilized copper ferrite aerogel. The objective is therefore to determine the optimal conditions for the degradation of model pollutants methylene blue (MB). MB was oxidized and degraded through the dark-Fenton process using Agar@GO-CuFe2O4 as a new biobased catalyst. The effect of the operating parameters was then evaluated to determine the optimal conditions. The degradation process was screened for different initial concentrations of dye solution between 10 and 150 mg/l, a volume range of H2O2 between 0.5 and 2.5 ml, and different pH from 2 to 7. The results show that 99.89 % of the MB with the initial concentration of 150 ppm was degraded by 20 mg of the catalyst and 2 ml of H2O2 (30 % W/W) at 40 °C and pH = 6. Pseudo-second-order kinetics satisfactorily describes the experimental data. The prepared catalyst can be applied to oxidize industrial effluents before they are released into the environment. Dye and textile industries are one of the main causes of water pollution and put the environment and health of society at risk. Developing new materials to decontaminate industrial waste effluents containing dyes as pollutants is challenging due to numerous issues, including tailoring recyclable and biodegradable agents. This study focuses on applying an advanced oxidation process, electro-Fenton for the treatment of dye-containing wastewater using agar-functionalized graphene oxide-immobilized copper ferrite aerogel. The objective is therefore to determine the optimal conditions for the degradation of model pollutants methylene blue (MB). MB was oxidized and degraded through the dark-Fenton process using Agar@GO-CuFe2O4 as a new biobased catalyst. The effect of the operating parameters was then evaluated to determine the optimal conditions. The degradation process was screened for different initial concentrations of dye solution between 10 and 150 mg/l, a volume range of H2O2 between 0.5 and 2.5 ml, and different pH from 2 to 7. The results show that 99.9 % of the MB with th