Relationship between the polymer/silica interaction and properties of silica composite materials

Cast film composites have been prepared from aqueous polymer solutions containing nanometric silica particles. The polymers were polyvinyl alcohol (PVA), hydroxypropylmethylcellulose (HPMC) and a blend of PVA‐HPMC polymers. In the aqueous dispersions, the polymer–silica interactions were studied through adsorption isotherms. These experiments indicated that HPMC has a high affinity for silica surfaces, and can adsorb at high coverage; conversely, low affinity and low coverage were found in the case of PVA. In the films, the organization of silica particles was investigated through transmission electron microscopy (TEM) and small‐angle neutron scattering (SANS). Both methods showed that the silica particles were well‐dispersed in the HPMC films and aggregated in the PVA films. The mechanical properties of the composite films were evaluated using tensile strength measurements. Both polymers were solid materials, with a high‐elastic modulus (65 MPa for HPMC and 291 for PVA) and a low‐maximum elongation at break (0.15 mm for HPMC and 4.12 mm for PVA). In HPMC films, the presence of silica particles led to an increase in the modulus and a decrease in the stress at break. In PVA films, the modulus decreased but the stress at break increased upon adding silica. Accordingly, the polymer/silica interaction can be used to tune the mechanical properties of such composite films. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1134–1146, 2006