Comparative electrochemical studies of zinc chromate and zinc phosphate as corrosion inhibitors for zinc

The anticorrosive performance of two inhibitive pigments, zinc chromate and zinc phosphate, was compared using electrochemical impedance spectroscopy (EIS) and the scanning vibrating electrode technique (SVET) in pigment extracts in 0.1 M NaCl. It was observed that zinc was protected from corrosion in both extracts. In tests using hot dip galvanised steel painted with an epoxy primer incorporating the pigments, the SVET detected the anodic and cathodic distribution along the scribes, although no significant differences were observed among the various primers. On the contrary, EIS was able to distinguish processes occurring on the metal surface exposed by the scribe in different samples. For primers with anticorrosive pigment, a time constant at high frequencies was attributed to a layer of protective nature, probably formed by metal ions from the substrate and inhibitive ions leached from the anticorrosive pigments.