Microstructure and hardness studies of the electron beam welded zone of Hastelloy C-276

Electron beam welding (EBW) technique is becoming popular in nuclear, chemical and aerospace industries due to its high penetration depth and fast cooling rate. Samples of Hastelloy C-276 have been welded by electron beam (EB). A scanning electron microscope (SEM) having the attachment of an energy dispersive system (EDS) has been employed to study the resulting microstructure and micro-eutectic phases. The microstructure of the molten zone (MZ) is found to be of fine lamellar type. The hardness of the MZ is found to be 35% higher compared to as-received alloy. The micro-eutectoids are rich in Mo and W. The X-ray diffraction patterns of the MZ show shifting of peaks towards higher angle compared to the diffraction pattern of the as-received alloy. Broadening of the peaks is also observed in the diffraction pattern of the MZ. Formation of the μ-phase was observed in the MZ after a tempering treatment at 950 °C.