3D Printing of Bi2Te3‑Based Thermoelectric Materials with High Performance and Shape Controllability

Thermoelectric (TE) energy conversion technology provides a promising way to improve the efficiency of fossil energy by generating electricity from low-grade waste heat. With regard to these applications, thermoelectric generators (TEGs) should be designed from system integration perspectives to simultaneously improve heat transfer efficiency and system simplification as well as the robust mechanical properties. However, typical TEGs fabricated by conventional methods barely accomplish such requirements. Herein, high-quality TEGs were assembled by combining the well-flowable spherical bismuth telluride (BT) powdered precursors and selective laser melting (SLM) technology. By optimizing the electronic and phonon transport properties through defect engineering driven by 3D printing, a high figure of merit was accomplished for 1.27 (p-type) and 1.13 (n-type) in BT. This achievement is primarily attributed to the nonequilibrium solidification mechanism, which leads to the formation of multiscale defects during the 3D printing process. The introduction of these multiscale defects enables the effective scattering of wide frequency phonons, leading to a substantial reduction in lattice thermal conductivity. Meanwhile, robust mechanical properties were obtained in the printed p-type/n-type BT TE materials parallel to the building direction (BD) with a compressive strength reaching 257/250 MPa by employing the fine grain structure and the high density of nanotwins introduced during the SLM process. A well shape-controllable and high-performance TEG was designed using 3D-printed BT half-rings, and an output power of 134 mW was achieved at a temperature gradient of 38.9 °C. Our study opens a new route for the great potential of TE materials based on standard commercial SLM 3D printing technology for low-grade waste heat emitted from structures with heterogeneous shapes.