Preparation of fully cross-linked CNBR/PP-g-GMA and CNBR/PP/PP-g-GMA thermoplastic elastomers and their morphology, structure and properties

Binary CNBR/PP‐g‐GMA and ternary CNBR/PP/PP‐g‐GMA thermoplastic elastomers were prepared by reactive blending carboxy nitrile rubber (CNBR) powder with nanometer dimension and polypropylene functionalized with glycidyl methacrylate (PP‐g‐GMA). Morphology observation by using an atomic force microscope (AFM) and TEM revealed that the size of CNBR dispersed phase in CNBR/PP‐g‐GMA binary blends was much smaller than that of the corresponding CNBR/PP binary blends. Thermal behavior of CNBR/PP‐g‐GMA and CNBR/PP blends was studied by DSC. Comparing with the plain PP‐g‐GMA, Tc of PP‐g‐GMA in CNBR/PP‐g‐GMA blends increased about 10 °C. Both thermodynamic and kinetic effects would influence the crystallization behavior of PP‐g‐GMA in CNBR/PP‐g‐GMA blends. At a fixed content of CNBR, the apparent viscosity of the blending system increased with increasing the content of PP‐g‐GMA. FTIR spectrum verified that the improvement of miscibility of CNBR and PP‐g‐GMA was originated from the reaction between carboxy end groups of CNBR and epoxy groups of GMA grafted onto PP molecular chains. Comparing with CNBR/PP blends, the tensile strength, stress at 100% strain, and elongation at break of CNBR/PP‐g‐GMA blends were greatly improved. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1042–1052, 2004