Environmental protection of titanium alloys in centrifugal compressors at 500 deg C in saline atmosphere

The use of the titanium alloy Ti-6246 (Ti-6Al-2Sn4Zr-6Mo, wt-%) for gas turbine compressors allows an increase in working temperature and stress level. Under severe service conditions, the material experiences combined high temperature and high mechanical stress and, in saline atmospheres, stress corrosion cracking (SCC) can occur, leading to catastrophic mechanical failure. The present study was performed to evaluate the potential of several surface treatments to protect Ti-6246 alloy, after salt deposit, from hot salt SCC at temperatures # < 500 deg C and 500 MPa static mechanical stress conditions. Shot peening, thermal oxidation and metal- ceramic coatings were investigated Experimental results confirm the existence of brittle stress corrosion phenomena marked by a low residual elongation of test samples and the presence of oxides on the fracture surfaces. Both shot peening and metal- ceramic coatings increase the hot salt SCC resistance of the alloy. Times to rupture were improved by a factor of 3 for shot peening and by a factor of 10 for metal-ceramic coatings. Inversely, the time to rupture of preoxidised alloys has been halved compared with uncoated alloys. As well as these interesting quantitative results, structural studies of metal-ceramic coatings showed that they are mechanically and chemically compatible with the titanium alloy substructure and should work under severe thermomechanical stresses and aggressive atmospheres.