Experimental analysis of the practical LBZ effects on the brittle fracture performance of cryogenic steel HAZs with respect to crack arrest toughness near fusion line
Focusing on crack arrest behavior, this study investigates the practical influence of local brittle zones (LBZs) on the brittle fracture resistance of heat-affected zones (HAZs) in advanced 9% Ni cryogenic steel welds, and discusses whether the LBZs of this steel in practice have potentially deleter...
Gespeichert in:
Veröffentlicht in: | Engineering fracture mechanics 2003-07, Vol.70 (10), p.1245-1257 |
---|---|
Hauptverfasser: | , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Focusing on crack arrest behavior, this study investigates the practical influence of local brittle zones (LBZs) on the brittle fracture resistance of heat-affected zones (HAZs) in advanced 9% Ni cryogenic steel welds, and discusses whether the LBZs of this steel in practice have potentially deleterious effects as previously thought, or not. By analyzing the variations in brittle crack arrest toughness (
K
a) and brittle crack initiation toughness (
K
c) within actual HAZ, it is found that LBZs of this steel may not be harmful in consideration of crack arrest toughness near fusion line. |
---|---|