Sn-containing (La,Mm)Ni5−xSnxH5−6 intermetallic hydrides: thermodynamic, structural and kinetic properties

This work focused on studies of the phase composition and crystal structure of LaxMm1−xNi4.7Sn0.3 (x=0, 0.5 and 1.0) alloys, where Mm denotes La-rich mischmetal produced by Norsk Hydro ASA. The alloys have been studied using conventional powder and synchrotron X-ray diffraction (XRD), powder neutron...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of alloys and compounds 2003-08, Vol.356-357, p.773-778
Hauptverfasser: Khyzhun, O.Yu, Lototsky, M.V., Riabov, A.B., Rosenkilde, C., Yartys, V.A., Jørgensen, S., Denys, R.V.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:This work focused on studies of the phase composition and crystal structure of LaxMm1−xNi4.7Sn0.3 (x=0, 0.5 and 1.0) alloys, where Mm denotes La-rich mischmetal produced by Norsk Hydro ASA. The alloys have been studied using conventional powder and synchrotron X-ray diffraction (XRD), powder neutron diffraction and scanning electron microscopy (SEM). After annealing at 950°C the alloys were nearly single-phase materials with small precipitations of RENiSn equiatomic intermetallics formed at grain boundaries. Hydrogen absorption–desorption studies at 298, 323 and 348 K showed (a) a ‘flat’ structure of the pressure–composition isotherms; (b) a rather broad range of working H storage capacities; (c) an increase of the plateau pressures and decrease in both enthalpy and entropy changes following an increase of the Mm content in the alloy; and (d) fast formation–decomposition rate. Desorption isotherms were approximated by a recently developed model of phase equilibria in the metal–hydrogen systems. In situ powder neutron diffraction studies of the system MmNi4.7Sn0.3–D2 show that in the region of α-solid solution deuterium insertion leads to a gradual increase of the unit cell volume reaching 1.9%. In the hexagonal β-MmNi4.7Sn0.3 D4.51 deuteride D atoms occupy two of four available types of tetrahedral interstices including 6m RE2(Ni,Sn)2 and 12n RE(Ni,Sn)3.