On The Causes Of Corrosion Fracture Of Industrial Pipelines
It is established that the most active corrosion components in gas- water-oil environment are hydrogen sulfide, carbon dioxide, oxygen, and mineral salts (especially chlorides). The main types of corrosion fracture of the metalware of oil and gas objects, in particular, industrial pipelines, exploit...
Gespeichert in:
| Veröffentlicht in: | Materials science (New York, N.Y.) N.Y.), 2003-05, Vol.38 (6), p.880-883 |
|---|---|
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | eng |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Zusammenfassung: | It is established that the most active corrosion components in gas- water-oil environment are hydrogen sulfide, carbon dioxide, oxygen, and mineral salts (especially chlorides). The main types of corrosion fracture of the metalware of oil and gas objects, in particular, industrial pipelines, exploited under severe climatic conditions, are static and cyclic hydrogen fatigue, sulfide cracking, and local (pitting and groove) corrosion. [Material: steel.] |
|---|---|
| ISSN: | 1068-820X |