Influence of Si and Ni on Surface Hot-shortness of Cu-Sn Containing Steel Heated in Water Vapor Containing Atmosphere

This paper describes the influence of Si and Ni on surface hot-shortness of 0.3%Cu-0.04%Sn containing steel heated in water vapor containing atmosphere, where the atmosphere was changed in a manner of x%H2O-1%O2-bal.N2 (x=0, 10, 20, 30). Surface hot-shortness was assessed by measuring the surface cracking depth occurring in the 1100°C hot-deformed specimens after 1250°C heating in the water vapor atmosphere. The microstructure at the scale/steel interface was closely observed and the effect of the mass gain on surface cracking depth was investigated. For lower than 0.01% Si steel, the surface cracking depth increased largely with the mass gain, while an addition of 0.1% Si seems to suppress the surface cracking, especially at increased mass gains and the change with the mass gain was small. Steels with 0.14%Ni-Si