Corrosion protection of AA 2024-T3 by bis-[3-(triethoxysilyl)propyl]tetrasulfide in neutral sodium chloride solution. Part 1: corrosion of AA 2024-T3

This study consists of two parts. In the first part, the corrosion of 2024-T3 aluminum alloy (AA 2024-T3) was studied using scanning electron microscopy and energy-dispersive X-ray spectroscopy. The results showed that the anodic S phase (Al 2CuMg) particles dealloyed Al and Mg during the 3.5 h of immersion in a neutral 0.6 M sodium chloride (NaCl) solution; with the dealloying of Mg being the most severe. Simultaneously, a heavy dissolution was also observed for the surrounding Al matrix of the S phase particles. This Al dissolution is likely to be caused by a local alkalization resulting from the coupled cathodic reaction (water and/or oxygen reduction). Such corrosion in AA 2024-T3, however, can be inhibited efficiently after the treatment of bis-[3-(triethoxysilyl)propyl]tetrasulfide (bis-sulfur silane). The associated studies on bis-sulfur silane treated AA 2024-T3 will be presented in the second part.