Thickness-dependent loss-induced failure of an ideal ENZ-enhanced optical response in planar ultrathin transparent conducting oxide films

Ultrathin planar transparent conducting oxide (TCO) films are commonly used to enhance the optical response of epsilon-near-zero (ENZ) devices; however, our results suggest that thickness-dependent loss renders them ineffective. Here, we investigated the thickness-dependent loss of indium tin oxide (ITO) films and their effect on the ENZ-enhanced optical responses of ITO and ITO/SiO multilayer stacks. The experimental and computational results show that the optical loss of ITO films increases from 0.47 to 0.70 as the thickness decreases from 235 to 52 nm, which results in a reduction of 60% and 45% in the maximum field enhancement factor of a 52-nm monolayer ITO and 4-layer ITO/SiO multilayer stack, respectively. The experimental results show that the ENZ-enhanced nonlinear absorption coefficient of the 52-nm single-layer ITO film is -1.6 × 10 cm GW , which is 81% lower than that of the 235-nm ITO film (-8.6 × 10 cm GW ), indicating that the thickness-dependent loss makes the ultrathin TCO films unable to obtain greater nonlinear responses. In addition, the increased loss reduces the cascading Berreman transmission valley intensity of the 4-layer ITO/SiO multilayer stack, resulting in a 42% reduction in the ENZ-enhanced nonlinear absorption coefficient compared to the 235-nm ITO film and a faster hot electron relaxation time. Our results suggest that the thickness and loss trade-off is an intrinsic property of TCO films and that the low-loss ultrathin TCO films are the key to the robust design and fabrication of novel ENZ devices based on flat ultrathin TCO films.