Polymer-Clay Nanocomposites Based on Blends of Polyamide-6 and Polyethylene

The preparation of polyamide‐6/clay, high‐density polyethylene/clay, and high‐density polyethylene/ polyamide‐6/clay nanocomposites is considered. X‐ray diffraction (XRD), differential scanning calorimetry (DSC), and Fourier Transform Infrared (FTIR) measurements show that the clay enhances the crystallization of the γ‐form of polyamide‐6. The clay also acts as a nucleation agent and causes a reduction of spherulitte size. Scanning electron microscopy (SEM) analysis of fracture surfaces shows that the clay reduces the PA‐6 particle size in the HDPE/PA‐6/clay nanocomposites and changes the morphology. Mechanical properties and the effect of maleated polyethylene are also reported. On considère la préparation de nanocomposites de polyamide‐6/argile, de polyéthylène/argile de haute densité et de polyéthylène/polyamide‐6/argile de haute densité. Des mesures de diffraction aux rayons X (XRD), de calorimétrie à balayage différentielle (DSC) et de spectroscopie infrarouge à transformée de Fourier (FTIR) montrent que l'argile améliore la cristallisation de la forme γ du polyamide‐6. L'argile agit également comme agent de nucléation et entraîne une réduction de taille des sphérolites. L'analyse par microscopie électronique à balayage (SEM) des surfaces de fractures montre que l'argile réduit la taille des particules de PA‐6 dans les nanocomposites HDPE/PA‐6/argile et modifie leur morphologie. Les propriétés mécaniques et l'effet du polyéthylène maléaté sont également décrits.