High-strength transition periods for welding structural steel in the quenched and tempered condition
The aim of this work was to select the transition piece for economically alloyed high-strength 30KhGSN2A steel in order to produce welded joints in quenched and tempered elements with a tensile strength of at least 1300 MPa. The main part of the investigations was carried out on 12 mm thick plates o...
Gespeichert in:
| Veröffentlicht in: | Welding international 2000-01, Vol.14 (10), p.817-821 |
|---|---|
| Hauptverfasser: | , , |
| Format: | Artikel |
| Sprache: | eng |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Zusammenfassung: | The aim of this work was to select the transition piece for economically alloyed high-strength 30KhGSN2A steel in order to produce welded joints in quenched and tempered elements with a tensile strength of at least 1300 MPa. The main part of the investigations was carried out on 12 mm thick plates of 30KhGSN2A steel. Plates 5, 10, 17 and 20 mm thick were also tested. |
|---|---|
| ISSN: | 0950-7116 1754-2138 |
| DOI: | 10.1080/09507110009549275 |