High-Temperature Stability of the Al2O3-LaPO4 System
The compatibility of Al2O3 and LaPO4 at temperatures up to 1600°C is examined. Provided the ratio of La to P was close to 1:1, no reactions were observed after 200 h at 1600°C. Moreover, the Al2O3/LaPO4 interface remained sufficiently weakly bonded to cause deflection of cracks, as reported previous...
Gespeichert in:
| Veröffentlicht in: | Journal of the American Ceramic Society 1998-04, Vol.81 (4), p.951-956 |
|---|---|
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | eng |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Zusammenfassung: | The compatibility of Al2O3 and LaPO4 at temperatures up to 1600°C is examined. Provided the ratio of La to P was close to 1:1, no reactions were observed after 200 h at 1600°C. Moreover, the Al2O3/LaPO4 interface remained sufficiently weakly bonded to cause deflection of cracks, as reported previously. In the presence of excess P or La, reactions occurred as expected, forming AlPO4 in the case of excess P, and LaAlO3 and LaAl11O18 in the case of excess La. |
|---|---|
| ISSN: | 0002-7820 1551-2916 |
| DOI: | 10.1111/j.1151-2916.1998.tb02432.x |