Densification of glass powders belonging to the CaO-ZrO2-SiO2 system by microwave heating

Densification and microstructural changes of two glassy compositions belonging to the wollastonite and zirconia stability fields in the ternary CaO-ZrO2-SiO2 system were studied in a 2.45 GHz multimode microwave cavity. The effect of microwaves is to lower the sintering and devitrification temperature with stronger influence for high zirconia content composition. Correlation was found between dielectric properties and heating rate, showing lower interaction temperature for high zirconia content composition which starts to absorb microwave energy at about 400 C compared to 800 C for the low-zirconia one. Sintering and crystallisation processes evolved in complex ways during heat treatment so that the two final glass-ceramic materials exhibit different microstructures, crystalline phases and mechanical properties. 10 refs.