Thermocyclic Behaviour of Microstructurally Modified EB-PVD Thermal Barrier Coatings

This paper focuses on the combined effects of substrate temperature and rotation during electron-beam physical vapor deposition (EB-PVD) on the columnar microstructure of yttria partially stabilized zirconia (YPSZ) thermal barrier coatings. Diameter and degree of ordering of the columns and the density of the coatings are sensitive to the processing parameters. Results are discussed in the frame of common structural zone models for PVD processes. The models are extended to consider the rotational effect. EB-PVD YPSZ TBCs of different column diameters were deposited on top of an EB-PVD NiCoCrAlY bondcoat on IN 100 superalloy test bars. The performance of the TBCs was investigated in a cyclic oxidation furnace test rig between 1100 C and 130 C and in a burner rig under hot gas corrosion conditions at a maximum temperature of 900 C. Results showed a correlation between cyclic lifetime and the various microstructures of the TBCs. Samples having a nonregular arrangement of columns performed best in both tests. (Author)