Release of millions of micro(nano)plastic fragments from photooxidation of disposable plastic boxes

The widespread use of disposable plastic boxes is exacerbating the dangers of microplastics (MPs); however, little is known about the fragmentation behavior of MPs during aging. In this study, the dynamic evolution on the release of micro(nano)plastics and photoaging properties of two disposable plastic boxes (polypropylene (PP) and polystyrene (PS)) were investigated under light irradiation and mechanical abrasion. Results showed that the weight of PP and PS was decreased by 53 % and 100 %, respectively after 60 d of ultraviolet irradiation (UV60). Moreover, a large number of fragmented particles were produced from the combined light irradiation and abrasion, with 0.142 ± 0.006 and 0.141 ± 0.013 million micro(nano)plastics/mL particles from PP and PS boxes, respectively, and the nanometer range (