Synthesis of a bifunctional epoxy monomer containing biphenyl moiety and properties of its cured polymer with phenol novolac

A new type of epoxy resin containing a 4,4′‐biphenylene moiety in the backbone (Bis‐EBP) is synthesized and confirmed by elemental analysis, infrared spectroscopy, and 1H‐nuclear magnetic resonance spectroscopy. In addition, to evaluate the influence of the 4,4′‐biphenylene group in the structure, an epoxy resin having a 1,4‐phenylene group in place of the 4,4′‐biphenylene moiety (Bis‐EP) is synthesized. The cured polymer obtained through the curing reaction between the new biphenyl‐containing epoxy resin and phenol novolac is used for making a comparison of its thermal and physical properties with those obtained from Bis‐EP and bisphenol‐A (4,4′‐isopropylidenediphenyl)‐type epoxy resin (Bis‐EA). The cured polymer obtained from Bis‐EBP shows markedly higher fracture toughness of 1.32 MPa m1/2, higher glass transition temperature, lower moisture absorption, and higher thermal decomposition temperature. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 74: 690–698, 1999