Effect of tartrate content on aging and deposition condition of copper–tin electrodeposits from a non-cyanide acid bath

The effect of the presence of tartrate additive on the chemical stability of a Cu–Sn acid bath was evaluated. It was observed that this additive hinders decomposition of the Cu/Sn deposition bath with storage time, since the decrease in electrochemical efficiency was attenuated. In addition, it was...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Surface & coatings technology 2002-08, Vol.157 (1), p.14-18
Hauptverfasser: Carlos, I.A, Bidoia, E.D, Pallone, E.M.J.A, Almeida, M.R.H, Souza, C.A.C
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The effect of the presence of tartrate additive on the chemical stability of a Cu–Sn acid bath was evaluated. It was observed that this additive hinders decomposition of the Cu/Sn deposition bath with storage time, since the decrease in electrochemical efficiency was attenuated. In addition, it was observed that optimal galvanostatic deposition with or without tartrate occurs at approximately 11 mA cm −2. However, in the presence of tartrate the deposition charge was lower, leading to lower energy consumption. SEM analysis showed that the tartrate added to the plating bath caused a marked change in the morphology of the Cu/Sn films obtained galvanostatically.
ISSN:0257-8972
1879-3347
DOI:10.1016/S0257-8972(02)00139-1