Preparation of polycrystalline YAG/alumina composite fibers and YAG fiber by sol–gel method

Polycrystalline yttrium–aluminum garnet, Y 3Al 5O 12 (YAG) fiber and α-alumina and YAG matrix composite fiber were prepared by the sol–gel method. α-Alumina and YAG matrix composite fiber with fine and homogeneous microstructure could be successfully fabricated by interpenetrating YAG in alumina matrix and adding α-alumina of seed particles to fibers. Effect of α-alumina seed particles and YAG on crystallization and microstructure of composite fiber were discussed. The size of alumina matrix of the composite fibers heated at 1600°C for 4 h was below 2 μm. The tensile of strength alumina fiber heat-treated at 1500°C was 0.2 GPa, while that of the composite fiber was 1.1 GPa.