Effect of Cervical Lesions on Fracture Resistance and Failure Mode of Maxillary Central Incisors Restored with Fiber Posts and Complete Crowns

To investigate the effect of a cervical cavity extending 1 mm apical to the cemento-enamel junction (CEJ) on fracture resistance and failure mode of maxillary central incisors that have been treated endodontically, present with complete and incomplete ferrules, and are restored with and without a fiber post. 50 intact human maxillary central incisors were divided into five groups (n=10): CG (control group) 6-mm fer-rule height, no cervical cavity, and without post; (CO) 6-mm ferrule height without post, with a cervical cavity (access to root canal and cervical cavity restored with composite resin), cervical cavity; and post with ferrule heights of 1 mm (CP1), 2 mm (CP2), and 6 mm (CP6) restored with fiberglass post and composite resin core. After complete metal crowns were cemented on all specimens, they were subjected to thermal cycling (6000 cycles, 5°C/55°C), followed by immediate testing of fracture resistance. After failure, the specimens were sectioned buccolingually to evaluate and identify the mode of failure. The data were analyzed with an analysis of variance (ANOVA) and the Student-Newman-Keuls multiple comparison tests (α =0.05). A 1-mm ferrule height (CP1) fracture resistance was significantly lower (531±125 N) compared to the 6-mm ferrule height (CP6) (769±175 N) (p