Nanometric boron nitride powders: Laser synthesis, characterization and FT-IR surface study

Boron nitride powders in the nanometric range were synthesized by laser driven reactions in BCl 3-NH 3 mixtures. The gaseous reactants were separately introduced in the beam of a high-powered continuous wave CO 2 laser. The powders with high specific surface area (up to 230 m 2g −1) present the turbostratic structure as characterized by TEM. The evolution towards the hexagonal structure by heating the powders up to 1920 K under nitrogen flow was followed by XRD. One BN powder has been fully characterized by infrared and Raman spectroscopies regarding bulk structure and identification of surface species as well. Bornitrid (BN) Pulver mit Nanometer-Korngrößen werden mit Hilfe eines CO 2 Dauerstrichlaser durch Pyrolyse aus dem Gasgemisch BCl 3-NH 3 gewonnen. Die Pulver mit hochspezifischer Oberfläche (bis zu 230 m 2g −1) weisen eine ‘turbostratische’ Struktur auf, wie eine TEM-Analyse es gezeigt hat. Die Entwicklung hin zur hexagonalen Struktur durch Erwärmung des Pulvers auf 1920 K unter Stickstoff wird von XRD gefolgt. Eines der BN Pulver konnte durch Infrarot- und Ramanspektroskopie vollständig charakterisiert werden, wobei außerdem chimisorbierte ‘Oberflächengruppen’ identifiziert wurden. Par pyrolyse de mélanges gazeux de BCl 3 et de NH 3, introduits séparément dans le faisceau d'un laser CO 2 continu, on synthétise des poudres nanométriques de nitrure de bore. La surface spécifique des poudres peut atteindre 230 m 2g −1. Une analyse MET met en évidence une structure turbostratique. L'évolution vers la structure hexagonale par chauffage des poudres sous flux d'azote jusqu'à 1920 K est suivi par DRX. On a caractérisé complètement une poudre de BN par spectrométrie infrarouge (FT-IR) et Raman, de plus les groupements chimisorbés en surface ont été identifiés.