Fracture Characteristics of SiC(p) / Al Composites
Several kinds of SiC(p)/Al composites fracture were observed. The fracture of the composites and the influence of technology process on the material fracture were discussed. The result shows that the morphology of the fracture surface of the composites looks like the matrix (commercial purity alumin...
Gespeichert in:
| Veröffentlicht in: | Rare metals 1994, Vol.13 (4), p.302-305 |
|---|---|
| 1. Verfasser: | |
| Format: | Artikel |
| Sprache: | eng |
| Schlagworte: | |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Zusammenfassung: | Several kinds of SiC(p)/Al composites fracture were observed. The fracture of the composites and the influence of technology process on the material fracture were discussed. The result shows that the morphology of the fracture surface of the composites looks like the matrix (commercial purity aluminum, Al-Li alloy and Al-Li-Zr alloy) the bonded SiC reinforcement hindered the crack propagation. Pressing in the process is in favor of the bonding between SiC and Al. |
|---|---|
| ISSN: | 1001-0521 1867-7185 |