Formation of lanthanum strontium cobalt thin films by metalorganic decomposition

Formation of lanthanum strontium cobalt thin films by metalorganic decomposition

Electrically conductive films of La0.5Sr0.5CoO3, 1 μm thick, were formed on a variety of substrates by metalorganic decomposition. The lowest resistivity films (1.2×10−3 Ω cm) were obtained on c-axis sapphire by annealing in oxygen at 800 °C. The film conductivity was limited by the diffusion of str...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Applied physics letters 1994-06, Vol.64 (25), p.3509-3511
Hauptverfasser: Mantese, Joseph V., Micheli, Adolph L., Catalan, Antonio B., Schubring, Norman W.
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Electrically conductive films of La0.5Sr0.5CoO3, 1 μm thick, were formed on a variety of substrates by metalorganic decomposition. The lowest resistivity films (1.2×10−3 Ω cm) were obtained on c-axis sapphire by annealing in oxygen at 800 °C. The film conductivity was limited by the diffusion of strontium into the substrate.
ISSN:0003-6951
1077-3118
DOI:10.1063/1.111256