Stress corrosion cracking susceptibilities of carbon steels in high temperature and high pressure water

Stress corrosion cracking susceptibilities of carbon steels in high temperature and high pressure water

The stress corrosion cracking (SCC) resistance of S45C steel in pure water high temperature and high pressure was studied. Its result was evaluated from point of view to develop high resistance steel for SCC. Susceptibility of SCC and mechanism of crack initiation process were examined under various...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Transactions of JWRI 1993-12, Vol.22 (2), p.257-261
Hauptverfasser: Matsuda, F, Kikuchi, Y, Kuroda, T, Liu, S-P, Sakaguchi, M, Kobayashi, M, Urayama, Y, Kuniya, J
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The stress corrosion cracking (SCC) resistance of S45C steel in pure water high temperature and high pressure was studied. Its result was evaluated from point of view to develop high resistance steel for SCC. Susceptibility of SCC and mechanism of crack initiation process were examined under various temperatures and dissolved oxygen concentrations as environmental factors using slow strain rate test.
ISSN:0387-4508