Preparation of transparent photoluminescence smart window by integration of rare‐earth aluminate nanoparticles into recycled polyethylene waste

Novel photoluminescent nanocomposite sheets were prepared for simple commercial manufacturing of transparent and luminous photochromic smart windows. A simple physical integration of lanthanide‐doped strontium aluminium oxide (LdSAO) nanoparticles into recycled polyethylene (PE) waste produced a smart nanocomposite with persistent phosphorescence and photochromic properties. Because the nanoparticle form of LdSAO is important for developing transparent materials, LdSAO nanoparticles were well dispersed in the PE matrix. Both the morphologies and chemical compositions of the LdSAO nanoparticles and LdSAO‐containing luminescent PE sheets were investigated. Both LdSAO‐free and photoluminescent PE sheets were colourless in normal daylight. However the LdSAO‐containing PE luminescent samples only exhibited a brilliant green colour under ultraviolet (UV) light and a greenish‐yellow colour in the dark as verified by Commission Internationale de l'éclairage laboratory parameters. Both absorbance and emission bands were monitored at 377 and 436/517 nm, respectively. The LdSAO‐containing PE luminescent sheets were compared with the LdSAO‐free sample using both photoluminescence spectroscopy and for their mechanical properties and were found to have improved scratch resistance, UV protection, and superhydrophobic activity. Due to the added LdSAO, photoluminescence, decay, and lifetime spectral tests confirmed its photochromic fluorescence and long‐lasting phosphorescence characteristics. The PE@LdSAO nanocomposite sheets displayed UV protection, photostability, hydrophobicity, and excellent durability compared with the blank LdSAO‐free PE sheet. A transparent photoluminescent smart window was prepared from polyethylene waste. Photochromism was monitored as a colour change to green under ultraviolet light. Long‐persistent phosphorescence was detected after extended time periods in the dark. The polyethylene‐based smart window displayed UV protection, superhydrophobic activity, high photostability, and excellent hardness.