Effects of hybrid inorganic-organic nanofibers on the properties of enamel resin infiltrants – An in vitro study

This in vitro study aimed to evaluate the overall mechanical properties of resin infiltrants doped with bioactive nanofibers and their ability in inhibiting enamel demineralization or achieving remineralization of the adjacent enamel to white spots. A commercial resin infiltrant (ICON, DMG) was doped with hybrid inorganic-organic nanofibers and analyzed for degree of conversion (DC, n = 3) and surface hardness (SH, n = 6). Subsequently, enamel specimens (6 × 4 × 2 mm3) were prepared and submitted to a demineralizing/remineralizing process to produce a subsurface caries-like lesion. The specimens were treated with one of the following materials: ICON infiltrant, DMG (control); ICON + nanofibers of poly-lactic acid (PLA)-filled with silica (PLA-SiO2); ICON + nanofibers of (PLA)-filled with calcium incorporated into a silica network (SiO2–CaP). Then, the specimens were subjected to a pH-cycling demineralizing/remineralizing model for 7 days at 37 °C. The %ΔSH change (after treatment), %SH loss and %SH recovery (after pH-cycling regimen) were calculated after SH evaluation (n = 9/group). The Ca/P weight ratio before and after pH-cycling regimen was evaluated through SEM/EDX. The results of DC were analyzed through the T-test (p