Preparation and evaluation of Pd-Sn modified Ru-Ir electrode for denitrification of high chlorine ammonia–nitrogen wastewater

In this paper, Pd-Sn modified Ru-Ir electrode was prepared by thermal oxidation method, and the effects of doping amount of Pd-Sn and synthesis conditions on Pd-Sn modified Ru-Ir electrode performance were studied. Linear sweep voltammetry(LSV), cyclic voltammetry(CV), and the Tafel curve were used to study the electrochemical performance of the Pd-Sn modified Ru-Ir electrode materials. The effects of the doping amount of Pd-Sn on the microstructure and valence states of Pd-Sn modified Ru-Ir electrode materials were investigated by SEM, TEM, XRD, and XPS. When the mass of Pd-Sn accounted for 1.5% of the total mass of the elements, the molar ratio of Ru-Ir was 2:1, and the molar ratio of Pd-Sn was 3:1; the LSV, CV, and the Tafel curves indicated that Pd-Sn modified Ru-Ir electrode had the lowest chlorine evolution potential (1.0640 V vs. SCE), the best CV curve coincidence, and the smallest corrosion current density (6.5 × 10 −4 A/cm 2 ), showing the best chlorine evolution performance, the best durability, and corrosion resistance; the characterization of SEM, TEM, XRD, and XPS showed that Pd-Sn was successfully doped into Ru-Ir electrode materials; the crystallinity of Pd-Sn modified Ru-Ir electrode was the highest, and the binding energy was the lowest, but the crystal form of Ru-Ir solid solution did not have changed. The optimal synthesis conditions of Pd-Sn modified Ru-Ir electrode material were as follows: Pd-Sn molar ratio was 3:1, calcination temperature was 500 ℃, calcination time was 4 h, and water was used as solvent. Pd-Sn modified Ru-Ir electrode can efficiently treat high chlorine ammonia–nitrogen wastewater, when the reaction volume was 200 mL, the initial concentration of NH 3 -N was 100 mg/L, the concentration of chloride ion was 5000 mg/L, the current was 0.75 A, and the reaction time was 40 min; the removal rate of ammonia nitrogen can reach 100%. Responsible editor: Weiming Zhang.