Effect of oxidation heat treatment with airborne-particle abrasion on the shear bond strength of ceramic to base metal alloys

Oxidation heat treatment has been studied to increase the metal-ceramic bond strength. However, information about its use with cobalt-chromium (Co-Cr) alloys is lacking. The purpose of this study was to evaluate the effect of oxidation heat treatment and oxidation heat treatment with alumina airborne-particle abrasion on the metal-ceramic bond strength of Co-Cr alloys compared with that of nickel-chromium (Ni-Cr) alloys. In total, 165 metal cylinders (∅5×8 mm) made of 5 base metal alloys were obtained by casting: 2 Ni-Cr (Fit Cast-SB and Fit Cast-V) and 3 Co-Cr alloys (Keragen, StarLoy C, and Remanium 2001). The specimens were divided into groups (n=11): no treatment, oxidation heat treatment, and oxidation heat treatment with airborne-particle abrasion. Oxidation heat treatment was performed starting at 650 °C and rising to 980 °C. The airborne-particle abrasion was performed with 100-μm alumina (0.2-MPa pressure, 5 seconds). One specimen had the surface topography and composition evaluated by scanning electron microscopy and energy dispersive X-ray spectrometry. The feldspathic ceramic was applied to the base metal alloy specimens (n=10). Shear tests were performed to obtain the metal-ceramic bond strength (MPa). The failure modes were evaluated. Data were evaluated by 2-way ANOVA and the Tukey post hoc test, Pearson correlation, and Fisher exact tests (α=.05). The group without treatment showed the highest roughness. The treatments increased oxygen and chromium levels and decreased nickel, molybdenum, and tungsten levels. Oxidation heat treatment provided an increase in metal-ceramic bond strength (P