Interface shapes during vertical bridgman growth of (Pb, Sn)Te crystals

Melt-solid interfaces obtained during vertical Bridgman growth of (Pb´, Sn)Te crystals were investigated with a quenching technique. The shapes of these interfaces, revealed by etching longitudinally cut sections, were correlated with the composition variations determined by electron microprobe analysis. These experiments demonstrated that the interface shape can be changed from concave to convex by moving its location from the edge of the cold zone into the hot zone. The metallography and microsegregation near the melt-solid interface were analyzed in detail. A sharp change in composition above the interface indicated the existence of a diffusion boundary layer of 40–90 μm thick. This small diffusion boundary layer is consistent with strong convective mixing in the (Pb, Sn)Te melt.