Hot-pressing of Bi-Pb-Sr-Ca-Cu-O superconducting thick film

Screen-printed Bi 1.84 Pb 0.34 Sr 2.03 Ca 1.9 Cu 3.06 O y superconducting thick films were prepared on MgO substrates from powder consisting almost entirely of the 110 K phase, and the thick film sandwiched between the two MgO substrates was further hot-pressed in air. Under the hot-pressing conditi...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Japanese Journal of Applied Physics 1990-06, Vol.29 (6), p.L875-L877
Hauptverfasser: MURAYAMA, N, HIRAMATSU, Y, TORII, Y
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Screen-printed Bi 1.84 Pb 0.34 Sr 2.03 Ca 1.9 Cu 3.06 O y superconducting thick films were prepared on MgO substrates from powder consisting almost entirely of the 110 K phase, and the thick film sandwiched between the two MgO substrates was further hot-pressed in air. Under the hot-pressing condition of 500 kg/cm 2 at 855°C for 30 min, the T c and resistivity at 270 K were 105 K and 6.1×10 -4 Ω·cm, respectively. The J c was 4800 A/cm 2 at 77 K in zero magnetic field. The relationship between superconducting properties and hot-pressing conditions was examined.
ISSN:0021-4922
1347-4065
DOI:10.1143/jjap.29.l875