Efficient and fast degradation of 4-nitrophenol and detection of Fe(III) ions by Poria cocos extract stabilized silver nanoparticles

In this study, a simple and environment-friendly method has been successfully applied for the production of silver nanoparticles (AgNPs) using Poria cocos extract. The reaction time of 60 min, the temperature of 90 °C, and silver ion concentration of 2.0 mM were identified as the best condition for the PC-AgNPs fabrication. The XRD analysis confirmed a highly crystalline face-centered cubic structure of the biosynthesized material. The PC-AgNPs were presented separately in a spherical shape with an average crystal size of 20 nm, as endorsed by the TEM and FE-SEM measurements. The presence and crucial role of biomolecules in stabilizing the nanoparticles were elucidated by FTIR, EDX, and DLS techniques. The prepared biogenic nanoparticles were further applied for the reduction of 4-nitrophenol (4-NP) and colorimetric detection of Fe3+ ions. The study results proved that PC-AgNPs exhibited superior catalytic activity and reusability in the conversion of 4-NP by NaBH4. The complete reduction of 4-NP could be achieved in 10 min with the pseudo-first-order rate constant of 0.466 min−1, and no significant performance loss was found when the material was reused five times. The colorimetric probe based on PC-AgNPs displayed outstanding sensitivity and selectivity towards Fe3+ ions with a detection limit of 1.5 μM in a linear range of 0–250 μM. Additionally, the applicability of the developed assay was explored for testing Fe3+ ions in tap water. PC-AgNPs have a great potential for further applications as a promising catalyst for reducing nitrophenols and biosensors for the routine monitoring of Fe3+ in water. [Display omitted] •Silver nanoparticles were produced using Poria cocos extract (PC-AgNPs).•The PC-AgNPs solution showed a high stability with a zeta potential of −47.3 mV.•PC-AgNPs exhibited excellent catalytic activity and stability in 4-NP reduction.•PC-AgNPs can be used as highly sensitive probes for the detection of Fe3+ ions.