MoS2 decorated on one-dimensional MgFe2O4/MgO/C composites for high-performance microwave absorption
[Display omitted] Advanced microwave absorption (MA) materials have attracted widespread attention to meet the challenges of electromagnetic (EM) pollution. Herein, MgFe2O4/MgO/C fibers were successfully prepared via electrospinning technology and carbonization, and their surfaces were coated by MoS...
Gespeichert in:
Veröffentlicht in: | Journal of colloid and interface science 2022-01, Vol.606, p.709-718 |
---|---|
Hauptverfasser: | , , , , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | [Display omitted]
Advanced microwave absorption (MA) materials have attracted widespread attention to meet the challenges of electromagnetic (EM) pollution. Herein, MgFe2O4/MgO/C fibers were successfully prepared via electrospinning technology and carbonization, and their surfaces were coated by MoS2 via hydrothermal method. The EM wave absorption performance of composites was enhanced due to the introduction of MoS2. The results showed that the EM wave absorption performance of MgFe2O4/MgO/C could not meet the requirements due to low dielectric loss and poor impedance matching. The performance of the composites was improved after coating of MoS2, which showed the strong wave absorption capability and the broad absorption bandwidth. The optimal reflection loss (RL) is −56.94 dB at 9.5 GHz and the effective absorption bandwidth is 3.9 GHz (8.08–11.98 GHz) with a thickness of 2.7 mm. The excellent MA performance can be mainly attributed to excellent synergistic effect between MgFe2O4/MgO/C and MoS2. Furthermore, MoS2 also contributes to dielectric loss and ideal impedance matching. MgFe2O4/MgO/C@MoS2 composites may be utilized for lightweight and high-efficient MA materials. |
---|---|
ISSN: | 0021-9797 1095-7103 |
DOI: | 10.1016/j.jcis.2021.08.056 |