Effect of an elastomeric urethane monomer on BisGMA-free resin composites containing different co-initiators

Objectives The aim of this study was to investigate the mechanical, chemical, optical, and adhesive properties of BisGMA-free experimental resin composites containing Exothane-24—an elastomeric urethane monomer—and different co-initiators. Materials and methods A blend of urethane dimethacrylate ( UDMA), extended dimethacrylate urethane (PEG 400), triethylene glycol dimethacrylate (TEGDMA), and camphorquinone was prepared. Two different co-initiators—dimethyl aminoethyl methacrylate (DMAEMA) or 4-N alcohol, N-dimethylamine phenylethyl (DMPOH)—were added to the blend. Exothane-24 monomer was added to the blend for each co-initiator and four groups were established as follows: DMAEMA; DMAEMA + Exothane; DMPOH; and DMPOH + Exothane. Specimens were photo-activated using a multi-wave LED light-curing unit (VALO; 954 mW/cm 2 of irradiance). Mechanical (ultimate tensile strength, flexural strength, flexural modulus and hardness), chemical (degree of conversion, hardness reduction, water sorption and solubility), optical (color change), and adhesive (microtensile bond strength) properties were analyzed. Data were submitted to two-way ANOVA and Tukey’s test ( α = 0.05). Results The resin composite containing DMPOH and Exothane-24 showed similar or superior performance to those of the other experimental composites for mechanical and chemical properties, except for flexural strength. It also showed less color change and greater micro-tensile bond strength. Conclusions Among the combinations tested, the BisGMA-free resin composite containing Exothane-24 combined with the DMPOH co-initiator showed the best mechanical, chemical, optical, and adhesive properties. Clinical relevance Exothane-24 monomer and DMPOH co-initiator could be useful in the formulation of BisGMA-free resin composites in order to minimize exposure to BPA.