Paint delamination from electrocoated automotive steels during atmospheric corrosion. I: Hot-dip galvanized and electrogalvanized steel

The mechanism of corrosion-induced paint delamination of electrocoated electrogalvanized and hot-dip galvanized automotive steels has been investigated. The materials were phosphated and electrocoated but not topcoated. The scribed panels were exposed to atmospheric conditions for 15 months. Two dis...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Journal of adhesion science and technology 1989, Vol.3 (1), p.1-27
Hauptverfasser:	VAN OOIJ, W. J, SABATA, A, LOISON, D, JOSSIC, T, CHARBONNIER, J.-C
Format:	Artikel
Sprache:	eng
Schlagworte:	Applications Applied sciences Automotive engineering Cross-disciplinary physics: materials science rheology Engineering techniques in metallurgy. Applications. Other aspects Exact sciences and technology Materials science Metals, semimetals and alloys Metals. Metallurgy Others aspects Physics Specific materials
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	The mechanism of corrosion-induced paint delamination of electrocoated electrogalvanized and hot-dip galvanized automotive steels has been investigated. The materials were phosphated and electrocoated but not topcoated. The scribed panels were exposed to atmospheric conditions for 15 months. Two distinct regions were observed in cross-sectioned samples: a delamination zone without corrosion products which preceded a zone where the coating forms corrosion products, which consist largely of ZnO/Zn(OH) sub 2 . The mechanism of delamination is postulated to be mechanical in nature. 19 ref.--AA
ISSN:	0169-4243 1568-5616