Translucency of nanoparticle-reinforced PMMA denture base material: An in-vitro comparative study

The aim of this study was to assess the translucency of denture base acrylic resin reinforced with zirconium dioxide (ZrO2NPs), silicon dioxide (SiO2NPs), and diamond (DNPs) nanoparticles. A total of 130 heat-polymerized acrylic discs (15×2.5 mm) were fabricated conventionally and divided into control and experimental groups according to nanoparticle type and concentration (0.5, 1, 1.5, and 2.5 wt%). Unmodified acrylic resin specimens served as control. All specimens were thermocycled (5,000 cycles). Translucency was measured using a spectrophotometer. ANOVA and post-hoc Turkeys’ test were used for data analysis at α=0.05. The translucency of modified PMMA was significantly lower than control (p0.05) which exhibited the highest translucency values among modified groups. As the NPs concentration increased, the translucency decreased and the lowest value was seen with 2.5% DNPs (1.18±0.10). The addition of ZrO2NPs, SiO2NPs, and DNPs into denture base resin decreased the translucency.