Statistical fibre failure and single crack behaviour in uniaxially reinforced ceramic composites

In order to compute a lower bound to the energy dissipation, a model assumes that matrix crumbling does not occur; fiber failure is governed by Weibull distirbution; failure occurs by a single matrix crack; and that the fiber/matrix interface is constrained by friction only. Results are compared to...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of materials science 1988-03, Vol.23 (3), p.928-933
1. Verfasser: SUTCU, M
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In order to compute a lower bound to the energy dissipation, a model assumes that matrix crumbling does not occur; fiber failure is governed by Weibull distirbution; failure occurs by a single matrix crack; and that the fiber/matrix interface is constrained by friction only. Results are compared to the energy dissipation before fiber failure previously computed.
ISSN:0022-2461
1573-4803
DOI:10.1007/BF01153991