Effects of thermal and mechanical cycling on the mechanical strength and surface properties of dental CAD-CAM restorative materials

The properties of dental computer-aided design and computer-aided manufacturing (CAD-CAM) materials vary. Studies regarding the effects of aging on the properties of these materials are lacking. The purpose of this in vitro study was to evaluate the changes in the mechanical and surface properties of different CAD-CAM materials after thermocycling and mechanical loading. In total, 150 bar-shaped specimens (17.0×4.0×2.0 mm) were prepared from feldspathic glass-ceramic (VM; Vitablocs Mark II), lithium disilicate glass-ceramic (EX; IPS e.max CAD), zirconia-reinforced lithium silicate glass-ceramic (CD; Celtra Duo), polymer-infiltrated ceramic network (VE; Vita Enamic), and resin-nanoceramic (CS; Cerasmart). Each type was divided into 2 groups (n=15; each). One group was subjected to thermocycling in distilled water at 5 °C to 55 °C for 6000 cycles and 50 N mechanical loading for 1.2×106 cycles. The other group was stored in 37 °C water for 24 hours. Nanoindentation hardness, Young modulus, and 3-point flexural strength were measured for the analyses of the mechanical properties. Surface roughness, surface microstructure, and elemental composition were measured to analyze the surface characteristics. Statistical analyses were performed with 1-way ANOVA with the Tukey HSD post hoc test, independent samples t test, Kruskal-Wallis test with Bonferroni post hoc test, Mann-Whitney U test, and 2-way ANOVA (α=.05). Before and after aging, CS exhibited the lowest hardness (1.20 to 1.04 GPa) and Young modulus (13.76 to 13.48 GPa) values (P