XPS and XES Study of the Valence Band of Cr-Al B.C.C. Solid Solutions

The XPS and Cr Lα ES valence band spectra of b.c.c. Cr‐Al alloys in the region 0 to 25 at% Al are presented. The shape and halfwidth of these spectra change notably at approximately 15 at% Al. The results are discussed on the basis of various simple models for the electronic structure of the alloys. The observed changes in the valence band are consistent with the results of magnetic and resistivity measurements. However, the present understanding of the changes in the electronic structure of the Cr‐Al alloys is not complete. The effect of the recently discovered inhomogeneity of the microstructure of these alloys in the upper part of the concentration region upon the electronic structure is, together with the antiferromagnetic order, the probable reason for the observed complicated behaviour of the valence band spectra with composition. Die XPS‐ und CrL‐Valenzbandspektren von k.r.z.‐Cr‐Al‐Legierungen im Konzentrationsbereich 0 bis 25 At% Al werden angegeben. Die Form und die Halbwertsbreite dieser Spektren verändern sich sichtbar bei etwa 15 At% Al. Die Resultate werden mit verschiedenen einfachen Modellen der Elektronenstruktur der Legierungen diskutiert. Die beobachteten Veränderungen des Valenzbands sind in Übereinstimmung mit Resultaten magnetischer und Widerstandsmessungen. Das gegenwärtige Verständnis der Ursachen dieser Veränderungen der Elektronenstruktur der Cr‐Al‐Legierungen ist jedoch unvollständig. Der Einfluß der kürzlich entdeckten Inhomogenität der Mikrostruktur dieser Legierungen bei größeren Konzentrationen auf die Elektronenstruktur ist eine wahrscheinliche Ursache für den beobachteten komplizierten Zusammenhang ihrer Valenzbandspektren mit der Zusammensetzung.