Stage III recovery in V-2% Zr alloy

Stage III recovery in V-2% Zr alloy

The recovery peak at 0.2 T sub m observed earlier in cold worked (1) and neutron irradiated vanadium was interpreted on the basis of migration of intrinsic defects. In recent studies on the recovery of dilute V alloys, the stage at approx 0.2 T sub m has been explained as being due to the migration...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of nuclear materials 1984-11, Vol.126 (3), p.321-322
Hauptverfasser: Pande, B.M., Anand, M.S., Agarwala, R.P.
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The recovery peak at 0.2 T sub m observed earlier in cold worked (1) and neutron irradiated vanadium was interpreted on the basis of migration of intrinsic defects. In recent studies on the recovery of dilute V alloys, the stage at approx 0.2 T sub m has been explained as being due to the migration of interstitial impurity atoms. Investigations carried out to study the recovery behaviour of cold worked and fast neutron irradiated V--2% Zr alloy are described. 9 ref.--AA
ISSN:0022-3115
DOI:10.1016/0022-3115(84)90045-X