In vitro fretting crevice corrosion damage of CoCrMo alloys in phosphate buffered saline: Debris generation, chemistry and distribution

Fretting crevice corrosion in modular tapers of total hip replacements has become a major concern in orthopedic medical devices. Solid and ionic debris arising from fretting crevice corrosion have been implicated in device failure and revision surgery. This study aims to use a 2D pin-on-disk fretting corrosion test system to visualize damage progression and debris generation during fretting corrosion of CoCrMo alloys in phosphate buffered saline (PBS). The results provide direct evidence of rapid debris generation during fretting corrosion (after only 12 min of testing). Debris was generated and either extruded from the contact region or impacted into adjacent crevice sites as long as fretting continued. After testing, the fretting region consisted of a damaged and plastically deformed contact region surrounded by a halo of fretting debris consisting entirely of oxides and phosphates within the crevice region. Evidence of pitting corrosion and grain boundary corrosion was observed. Solid debris consisted of chromium (Cr), phosphate (P) and oxygen (O). X-ray photoelectron spectroscopy analysis of the near-fretted metal surface area showed a thicker oxygen (O1s) containing film with the depth profile of O1s above 10% penetrating up to 5.75 nm while the O1s concentration on the unfretted area fell to below 10% after 1 nm depth. Ion concentration in the PBS, measured using inductively coupled mass spectrometry, showed cobalt (Co) ions were most prevalent (1.46 ppm) compared to chromium (Cr) (0.07 ppm) and molybdenum (Mo) (0.05 ppm) (p